Aluminum Tube / Pipe
The advantages of aluminum alloy are lightweight, excellent electrical and thermal conductivity, high corrosion resistance and ductility.
Aluminum alloy is soft and usually alloyed with copper, zinc, magnesium, silicon, manganese and lithium to increase strength. When aluminum alloy is exposed to air, an anti-oxidant coating will be formed instantly to protect products. Aluminum alloy is one of the lightest metals. The application of products ranges from precision technology to daily commodities.
Mechanical Properties
Tensile Strength, Ultimate
120 ~ 420
Mpa
Tensile Strength, Yield
60 ~ 300
Mpa
Hardness, Brinell
40 ~ 108
Product Specification and Size :
Standard Specification: GB/T 6892, GB/T 6893, ASTM B221, EN754, EN 755
Available Specification
Alloy and Temper
Alloy | Temper |
|---|
5xxx: 5052, 5083, 5754 | O, H14, H112 |
6xxx: 6005, 6060, 6061, 6063, 6082, 6463 | O, T4, T5, T6, T66, T6511 |
Alloy Designation (For Reference)
Comparison of Alloy Designations for Aluminum Products
Alloy Series | Chinese Standard | American Standard | European Standard |
|---|
5xxx Series | 5052 | 5052 | EN AW-5052 |
5xxx Series | 5083 | 5083 | EN AW-5083 |
5xxx Series | 5754 | - | EN AW 5754 |
6xxx Series | 6005 | 6005 | - |
6xxx Series | 6060 | 6060 | EN AW-6060 |
6xxx Series | 6061 | 6061 | EN AW-6061 |
6xxx Series | 6063 | 6063 | EN AW-6063 |
6xxx Series | 6082 | 6082 | EN AW-6082 |
6xxx Series | 6463 | 6463 | - |
Temper Designation (For Reference)
Temper | Definition |
|---|
O | Annealed |
H14 | Strain Hardened, 1/2 Hard |
H112 | Slightly strain harden from working at an elevated temperature or from limited amount of cold work |
T4 | Solution heat-treated and naturally aged |
T5 | Cooled from an elevated temperature shaping process and then artificially aged |
T6 | Solution heat-treated and then artificially aged |
T651 | Solution heat-treated, stress-relieved by stretching a controlled amount and then artificially aged |
T66 | Solution heat-treated and then artificially aged - mechanical property level higher than T6 achieved through special control of the process (6000 series alloys) |
T6511 | Solution heated-treaded, stress-relieved by stretching a controlled amount and then artificially aged. Minor straightening is allowed after stretching to comply with standard tolerances |
Available Size Range
Temper | Definition |
|---|
Outside | 8.0~350mm for Round |
Diameter | 15x15mm~250x250mm for Square 10x20mm~200x250mm for Rectangle |
Wall Thickness | 1.0~40mm |
Length | 1,000~6,000mm |
- Production Process: Extruded, Cold Drawn
- Form & Image: Round, Square, Rectangle
- Surface Finish: Mill Finish, unless otherwise specified
- Surface Protection: Paper interleaved
Application
Aluminum alloy tube and pipe can be widely used in construction, machinery, electronics, sports equipment, advertising, transportation, consumer goods, furniture, aviation, military and other applications. We also provide anodizing, bending, welding, polishing and punching service.
Chemical Composition (For Reference)
Chemical Composition conforms to Chinese, American and European standard specification
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others:Each | Others:Total | Al: Min. |
|---|
5052 | 0.25 | 0.40 | 0.10 | 0.10 | 2.20~2.80 | 0.15~0.35 | 0.10 | - | 0.05 | 0.15 | remainder |
5754 | 0.40 | 0.40 | 0.10 | 0.50 | 2.60~3.60 | 0.30 | 0.20 | 0.15 | 0.05 | 0.15 | remainder |
5083 | 0.40 | 0.40 | 0.10 | 0.40~1.0 | 4.0~4.90 | 0.05~0.25 | 0.25 | 0.15 | 0.05 | 0.15 | remainder |
6060 | 0.30~0.60 | 0.10~0.30 | 0.10 | 0.10 | 0.35~0.60 | 0.05 | 0.15 | 0.10 | 0.05 | 0.15 | remainder |
6061 | 0.40~0.80 | 0.70 | 0.15~0.40 | 0.15 | 0.80~1.20 | 0.04~0.35 | 0.25 | 0.15 | 0.05 | 0.15 | remainder |
6063 | 0.20~0.60 | 0.35 | 0.10 | 0.10 | 0.45~0.90 | 0.10 | 0.10 | 0.10 | 0.05 | 0.15 | remainder |
6082 | 0.70~1.30 | 0.50 | 0.10 | 0.40~1.0 | 0.60~1.20 | 0.25 | 0.20 | 0.10 | 0.05 | 0.15 | remainder |
6463 | 0.20~0.60 | 0.15 | 0.20 | 0.05 | 0.45~0.90 | - | 0.20 | - | 0.05 | 0.15 | remainder |